# What makes Gorilla Glass more durable with each generation?

Gorilla Glass (GG) is one of the most recognizable brands of toughened glasses today, thanks to their marketing and widespread usage in various gadgets and automobile industry.

According to Wikipedia, it's basically an ion exchange ($$\ce{Na+ <-> K+}$$) within the glass (boro-/alumosilicate?) matrix which gives this material resistivity against scratches and various mechanical impacts:

Still, there is a new generation of GG released every few years, showing better properties with thinner samples, making me think it's all not just about ion exchange.

Are there other ways of "chemical strengthening" besides cationic exchange that can be utilized to strengthen the glass, keeping it flexible and less fragile at the same time?

• I believe that may be classified information that Corning wouldn't want to let other competitors know. – Pritt says Reinstate Monica Jul 4 '17 at 10:16
• @PrittBalagopal That's why I'm asking. I'm also curious whether community can beat their best chemists. – andselisk Jul 4 '17 at 10:17
• "...can beat their best chemists" Corning doesn't just hire chemists, they more over hire glass scientists that have bachelors/PhD's in glass or materials science. – A.K. Mar 14 at 14:47
• @andselisk If you'd pay me more then they're paid. ;) – Mithoron May 21 at 21:14

Are there other ways of "chemical strengthening" besides cationic exchange that can be utilized to strengthen the glass, keeping it flexible and less fragile at the same time?

In a word: No.

To understand why ion exchange strengthens glass, you have to understand why the ion exchange makes the glass harder. The process ion exchange hardening, its done at a temperature that allows ion diffusion, but disallows a reconfiguration of the glass structure or relaxation of bonds (below Tg). When sodium atoms are replaced by potassium in glass, the potassium ions occupy a site that is sized for sodium; this mismatch creates the compression that in turn gives the glass its scratch resistance. Thus the only way to chemically harden the glass is to substitute larger ions into the glass.

Now an astute person might be thinking:

Are there other ways of "chemical strengthening" besides cationic exchange... What about anion exchange?

To this yes in theory if you could substitute the anions without rearranging the structure then yes anion exchange would be another way. But as Yogi Berra once said "in theory there's no difference between theory and practice, but in practice there is." The problem with anion exchange is you would be breaking and thus relaxing the bonds of atoms that you need to remain in place, thus no strengthening would occur.

I suppose you could also modify the surface to make a layer of silicon nitride or carbide and call that anion exchange, but would it this strengthening glass or changing the material altogether?

One way in which you could increase glass strength though still predominately a chemical process is to substitute sodium for lithium (or hydrogen), anneal the glass to allow the bonds to relax to form sites sized for lithium then substitute potassium back in where the lithium is to make it even stronger.

As far as what make each generation of GG stronger, I think it is base glass improvement such as modifying the aluminum content or making the glass thinner or making the ion diffusion more local to the surface and preventing the potassium from penetration too far.

• @andselisk I won't edit this into the answer until I find a paper that corroberates it, but it has been alleged to me that high pressure argon could diffuse into the interstitial sites at elevated temperatures creating additional compression in anterior regions further strengthening the glass. – A.K. Aug 22 at 17:46

To really answer this, you need to characterize the glass in terms of its properties, and not something like its ability to resist being scratched. Scratch resistance is a behaviour, and not a property. There are many ways of making something more scratch resistant.

"Hardness" itself is a behaviour, and not a property.

In any case, it might be that they're onto a very good toughening mechanism here, with various degrees of ion exchange, and they can tweak the process a lot and still get improvements.

Controlling the ions present in the glass matrix is going to affect both the residual stresses of the total glass layer, as well as the properties of each layer. And that will affect hardness/scratch resistance and toughness.

In most materials, toughness and hardness are in competition. But in a brittle material like glass, fracture needs a defect to initiate from. So if you adjust the cations present in the glass matrix to make the surface layer hard, it is potentially brittle. But if you also make it in compressive stress compared to the inner region, it become tougher.

There won't be just one way to achieve this, as in its not a single optimized point, but rather a response surface. So as they understand the process better, they can move along that response surface, and show improvements every few years.

• I'd disagree that " 'Hardness' itself is a behaviour, and not a property." Minerals are absolutely classified by hardness. The problem with glasses is that they don't have a definite chemical formula like a mineral, so there is no characteristic hardness value. – MaxW Sep 23 '17 at 4:03