I'm not a chemist but I remember that the standard HF/nitric silicon etch used in micro-fabrication supposedly worked in two steps; the HF would dissolve the thin SiO2 oxide layer on the silicon surface, exposing silicon atoms, and the nitric acid would then re-oxidize the bare silicon, allowing the HF to then dissolve it.

Or at least that's how it was explained to me.

Despite being challenged here, Wikipedia explains that the aluminum bits in sodium hydroxide-based drain cleaner are included to produce heat via exothermic liberation of hydrogen gas so that the heat can loosen some of the clogging materials. The article provides the following two steps.

  1. Breakdown of Aluminum Oxide: $\ce{ \ \ \ Al2O3 + 2NaOH + 3H2O → 2Na [Al(OH)4]}$

  2. Oxidation of Aluminum metal: $\ce{ \ \ \ 2Al + 2NaOH + 6H2O → 2Na[Al(OH)4] + 3H2}$

Is what is happening similar to my understanding of the HF/nitric etch of silicon; it is the oxidized aluminum that is removed by the solution, and only because it happens to also oxidize the freshly exposed aluminum metal that the oxide is removed?

Snapshot of some drain cleaner with aluminum bits

Snapshot of some drain cleaner with aluminum bits

  • $\begingroup$ That last sentence is a bit confusing, maybe you can explain the mechanism you are talking about in a little more detail. $\endgroup$
    – Buck Thorn
    Commented Jan 12, 2020 at 11:56
  • $\begingroup$ @BuckThorn the first four words of the first sentence are "I'm not a chemist..." so i this case maybe I can not. However the miracle of Stack Exchange allows those who understand better to post answers, and that is exactly what has happened. $\endgroup$
    – uhoh
    Commented Jan 12, 2020 at 12:15
  • $\begingroup$ The question is about logic and usage of language. Perhaps read this again: "only because it happens to also oxidize the freshly exposed aluminum metal that the oxide is removed?" $\endgroup$
    – Buck Thorn
    Commented Jan 12, 2020 at 12:18
  • $\begingroup$ @BuckThorn if there is no oxidation, then logically there will be no more oxide to be removed, and therefore aluminum dissolution will cease. I'm not getting what it is that you are asking me to clarify. $\endgroup$
    – uhoh
    Commented Jan 12, 2020 at 12:22
  • 1
    $\begingroup$ @BuckThorn except that I've asked it in a form of a question, yes I think so. $\endgroup$
    – uhoh
    Commented Jan 12, 2020 at 12:28

1 Answer 1


If you want to understand the reaction of $\ce{NaOH}$ on Aluminium, you may describe it this way. First, the aluminium reacts spontaneously with water, like sodium or calcium, producing gaseous Hydrogen $\ce{H2}$ and an metallic oxide or hydroxide. With sodium or calcium, the hydroxide produced by this reaction quits the metal surface, and get dissolved, leaving a fresh surface of metal ready to react with more water. The reaction with sodium is:

$$\ce{2 Na + 2 H2O -> 2 NaOH + H2}$$

With aluminium, it is not the case. The reaction is:

$$\ce{4Al + 6 H2O -> 2 Al2O3 + 6 H2}$$

But the aluminium oxide is not soluble into water and it makes a waterproof layer on the surface of the metal, which prevents further contact between the metal and water. So the reaction stops, due to this protecting effect of $\ce{Al2O3}$.

There are two ways of allowing the reaction to continue:

  1. Dissolve $\ce{Al2O3}$ as soon as it is produced by adding $\ce{NaOH}$, as @Uhoh tells it in its first equation.
  2. Prevent the $\ce{Al2O3}$ oxide layer from adhering on the metal surface by adding some mercury salt in the water. In this case the mercury ions $\ce{Hg^{2+}}$ may go through the oxide layer, reacts with the metal and produces a mercury deposit which forms an alloy with Aluminium. The reaction is:

$$\ce{2Al + 3 Hg^{2+} -> 2 Al^{3+} + 3Hg}$$

The $\ce{Al2O3}$ layer cannot adhere on the surface of this alloy Al-Hg. So the reaction with water continues as long as there is some mercury atoms left on the metallic surface.

So, to go back to @Uhoh's question, it is not $\ce{NaOH}$ that acts on Aluminium. It is water. The action of $\ce{NaOH}$ is to remove the oxide layer.

  • $\begingroup$ okay so somewhat like the HF/nitric combination example dissolves silicon in two steps, this NaOH/water combination dissolves aluminum also in two steps; the NaOH removes the oxide and the water is sufficient to quickly re-oxidize the freshly exposed aluminum, and because aluminum is so incredibly reactive it happens fast enough that a more powerful oxidizer (like the HF in the silicon case) is not needed. Thanks! $\endgroup$
    – uhoh
    Commented Jan 12, 2020 at 12:19
  • 1
    $\begingroup$ You are right ! $\endgroup$
    – Maurice
    Commented Jan 12, 2020 at 12:54